電熔白色氧化鋁砂24#

電熔白色氧化鋁砂24#是剛玉的一種，氧化鋁含量99%以上。噴砂用氧化鋁砂的粒徑范圍經過嚴格控制，使磨粒大小控制在一定范圍內。噴砂后產生表面一致的粗糙度。白剛玉韌性好，研磨能力強，自銳性好，噴射到噴砂工件表面時，通過氣流的沖擊力，工件撞擊出凹痕。鈍化后的噴砂表面有利于后續噴漆的油漆保持把持力。白剛玉噴砂磨粒還具有噴砂效率高，利用率高的優點。

White fused aluminum oxide 24# is a type of corundum, with an alumina content of over 99%. The particle size range of aluminum oxide sand used for sandblasting is strictly controlled, ensuring that the abrasive particle size is controlled within a certain range. After sandblasting, a consistent surface roughness is produced. White corundum has good toughness, strong grinding ability, and good self sharpening. When sprayed onto the surface of sandblasted workpieces, the impact force of the airflow causes the workpieces to collide with dents. The sandblasted surface after passivation is beneficial for maintaining the grip of subsequent paint spraying. White alumina sandblasting abrasive particles also have the advantages of high sandblasting efficiency and high utilization rate.

電熔氧化鋁砂的特性：
1.    白剛玉顯微硬度20.58Gpa,維氏硬度2200-2400kg/mm2，莫氏硬度9.0。可噴砂于大部分金屬、鑄鋼件、鑄鐵件、有色金屬合金材料、含鉻含錳含鎢鉬金屬、玻璃和其他非金屬材料。
2.    白剛玉研磨能力強，噴砂效率高，由于具有很強的自銳性，不會對噴砂表面造成燒*氧化。
3.    白鋼玉還可以直接用于研磨拋光，表面處理，噴砂除銹等領域，可用于干式和濕式噴砂，表面拋毛拋光，噴涂前表面處理鈍化等領域。
4.    白鋼玉氧化鋁的純度高，主要晶相時α相的氧化鋁。雜質少，磁性物含量低，噴砂后不會產生化學殘留，可用于醫藥、航空、食品領域機械部件的噴砂。

電熔氧化鋁砂的物理指標：

顏色	白色
硬度	莫氏9.0
使用溫度	1900 ℃
熔點	2250 ℃
比重	3.95g/cm3
體積密度	3.6g/cm3
堆積密度	1.55-1.95 g/cm3
晶形	多棱角

電熔氧化鋁砂化學成分：

	白剛玉粒度砂 F8-F220	白剛玉微粉 F230-F2000
AL₂O₃	99.53%	99.27%
SiO₂	0.06%	0.14%
NA₂O	0.23%	0.28%
Fe₂O₃	0.07%	0.06%
CaO	0.03%	0.05%

氧化鋁砂的用途：

樹脂結合劑砂輪，陶瓷結合劑砂輪，涂附磨具的原材料。
噴砂鈍化去氧化層，做金屬噴涂前的表面預處理。
非金屬例如亞克力、陶瓷復合材料、裝飾玻璃的表面亞光磨砂效果噴砂。
耐磨砂，高溫墊砂等。